Product Information | |
Name | Custom 455 Ageing Hardened Steel |
Equivalent Grade: | AMS 5617,UNS S45500,ASTM A564,XM-16 |
Condition of delivery: | Hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering |
Surface condition | Scaled (hot working finished)/ground/rough machining/fine machining |
Product Shape available: | Round,Flat,Square,Hexagon,Plate,Sheet,Other |
Customs HS code: | 72221100 |
Third-party Inspection: | SGS, TUV, or CNAS |
Material origin From: | P. R, China. |
Terms of price: | Ex works, CIF, CFR. |
Mode of transportation: | Sea Shipment, Air Cargo, or International Express. |
Certification For Exportation: | Invoice, Packing list, Bill of lading, and Origin of Certificate. |
Min.order quantity per batch: | 3300 KG |
Heat Treatment Practice: | Quenched 870 ℃,water/oil cooled, tempered 550 ℃, air cooled. |
UT test standards: | ASTM E2375 / SAE AMS 2154 / EN 10228-3. |
Meltling Process Route: | BEF + ESR / EAF + LF + VD + ESR |
Standard Export Packing Way: | Wooden box, wooden tray with free from fumigation. |
Production Lead Time: | Within 70 ~ 90 days after downpayment. |
Description
Chemical Composition
|
►GENERAL CHARACTERISTICS OF STAINLESS STEEL Custom 455 SteelThis is a martensitic, age-hardenable stainless steel with good atmospheric corrosion resistance. The alloy is soft and formable when annealed and may be brought to high strengths by a single-step aging treatment, while maintaining good ductility and toughness.APPLICATIONS This alloy should be considered where a combination of simplicity of heat treatment, ease of fabrication, high strength and corrosion resistance is required. Excellent resistance to oxidation is obtained up to 1100ºF (595ºC). FORGING The alloy is easily forged within the temperature range 2300/1650F (1260/900ºC), but for optimum grain size and mechanical properties the material to be forged should be uniformly heated to 1900/2100ºF (1040/1150ºC), soaked and forged to finish at 1700/1500ºF (930/815ºC). Forgings should be air cooled and then annealed. HEAT TREATMENT Solution treatment/annealing is carried out at 1500/1550ºF (815/845ºC) for a one hour soak, followed by rapid cooling. Age/precipitation hardening is performed at 900/1050ºF (480/570ºC) for 4 hours, followed by air cooling. An optimum combination of strength, ductility and toughness results from the 900ºF (480ºC) treatment. MACHINABILITY The machining characteristics of this alloy are similar to those of the nickel maraging steels. Rigid tooling and equipment, slow speeds and positive feeds are required, along with adequate quantities of coolant. WELDABILITY The alloy is readily welded by the shielded fusion and resistance processes. Oxyacetylene welding is not recommended due to the danger of carbon pickup in the weld area. No preheat is required when welding this alloy.An optimum combination of strength, ductility and corrosion resistance is obtained by solution annealing welded parts prior to aging. ►Custom 455 Steel Chemical Composition
►Custom 455 Steel Mechanical Properties
|