Product Information | |
Name | Martensitic Stainless S42200 Round bars Tube Processing |
Stocklist & Inventory Available: | Diameter 20 ~ 300mm |
Material Specification: | ASTM,AISI,UNS,AMS,Werkstoffe,Miscellaneous |
Equivalent Grade: | AMS 5655,UNS S42200,ASTM A565,1.4935,AISI 422,10705BU,X20CrMoW12-1 |
Condition of delivery: | Hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering |
Surface condition | Scaled (hot working finished)/ground/rough machining/fine machining |
Product Shape available: | Round,Flat,Square,Hexagon,Plate,Sheet,Other |
Customs HS code: | 72223000 |
Third-party Inspection: | SGS, TUV, CCIC |
Material origin From: | P.R.China |
Terms of price: | Base on Ex works, CFR, CIF |
Mode of transportation: | Sea shipment, Air cargo |
Certification For Exportation: | MTR, COC, CO, Invoice and packling list |
Min.order quantity per batch: | 1250 kg |
Heat Treatment Practice: | Hardened 1030 ℃, water or air cooled, tempered 650 ℃, double tempered. |
Output Per Year: | 18000 ton |
UT test standards: | EN 10308, MIL-STD-AMS 2154 CL A |
Meltling Process Route: | BEF + AOD / EAF + LF + VD / + ESR/VAR |
Standard Export Packing Way: | wooden box, Pallet |
Production Lead Time: | Within 60 days after deposit 30% in advance |
Description
Chemical Composition
Mechanical Properties
|
►GENERAL CHARACTERISTICS OF STAINLESS STEEL Stainless Steel UNS S42200Stainless type S42200 is a hardenable steel good for service temperatures to 1200ºF (650ºC), and capable of heat treatment to high mechanical property values.►Stainless Steel 422 Inventory Size Ranges
APPLICATIONS OF STAINLESS S42200 Buckets and blades in compressors and steam turbines, forged high-temperature bolting, compressor and turbine wheels, valves and valve trim and aircraft parts FORGING STAINLESS S42200 Large sections should be preheated to 1200/1400ºF (650/760ºC), then to 1900/2150ºF (1040/1175ºC). Forgings should be slow cooled and annealed or tempered as soon as possible after reaching room temperature. Hardening should not be attempted without an inter anneal or preheat in the range 1200/1400ºF (650/760ºC.) ►Stainless Steel S42200 Chemical Composition
Please contact us for more details. The technical data provided is for information only and not for design purposes.►Stainless Steel S42200 Mechanical Properties
Please contact us for more details. The technical data provided is for information only and not for design purposes. |