| Product Information | |
| Name | AMS 5623 Nonmagnetic Steels |
| Material Specification: | AMS 5623B |
| Equivalent Grade: | UNS K91456 |
| Condition of delivery: | hot rolled / forged, solution treated |
| Surface condition | bright finished / ground / rough machined |
| Product Shape available: | Round bars, flat bars, forgings, ring |
| Third-party Inspection: | SGS, TUV, CCIC |
| Material origin From: | P.R.China |
| Terms of price: | Base on Ex works, CFR, CIF |
| Mode of transportation: | Sea shipment, Air cargo, and Express |
| Certification For Exportation: | MTR, COC, Certificate of origin,FOMR A/E, Invoice and packling list |
| Min.order quantity per batch: | 1250 kg |
| Heat Treatment Practice: | Solution 1050 ℃, water or air cooled |
| UT test standards: | EN 10308, MIL-STD-AMS 2154 CL A |
| Meltling Process Route: | BEF + AOD |
| Standard Export Packing Way: | Wooden box / tray free from fumigation |
| Terms of payment: | Bank wire |
| Production Lead Time: | Within 65 days after deposit 40% in advance |
|
Description
|
This alloy is generally smelt in Basic Electric Furnace (EAF, AOD) or VIM + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement. It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on. Main Chemical Elements (mass weight %) Carbon, C (％): 0.55 ~ 0.65 Silicon, Si (％): ≤ 1.00 Manganese, Mn (％): 5.00 ~ 6.00 Phosphorus, P (％)≤: 0.035 Sulfur, S (％)≤: 0.025 Chromium, Cr (％): - Nickel, Ni (％): 8.50 ~ 10.5 Molybeenum, Mo (％): ≤ 0.50 Typical Mechanical Properties AT RM. Condition: solution annealed Tensile strength σb≥/MPa: 700 Yield strength σs≥/MPa: 300 Elongation δ5≥(%): 55.0 AKU≥/J: 300 min. Hardness HBS: - Condition: work hardened Tensile strength σb≥/MPa: - Yield strength σs≥/MPa: - Elongation δ5≥(%): - AKV≥/J: - Hardness HBS: 149 ~ 179 |