Product Information | |
Name | AISI 422 & Grade 616 & ASTM B4B Martensitic Stainless |
Stocklist & Inventory Available: | Round bars dia. 20 ~ 230mm |
Material Specification: | ASTM A565 |
Equivalent Grade: | AMS 5655 / UNS S42200 / 1.4935 / AISI 422 / 10705BU |
Condition of delivery: | Hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering |
Surface condition | Rough turned bright |
Product Shape available: | Round bars, flat bars, forgings, ring |
Third-party Inspection: | SGS, TUV, CCIC |
Material origin From: | China |
Terms of price: | Ex works, CFR |
Mode of transportation: | Sea shipment, Air cargo, and Express |
Certification For Exportation: | MTR, COC, CO, Invoice and packling list |
Min.order quantity per batch: | 1000 Kg |
Heat Treatment Practice: | Hardened 1030 ℃, water or air cooled, tempered 650 ℃, double tempered. |
Output Per Year: | 15500 ton |
UT test standards: | EN 10308, MIL-STD-AMS 2154 CL A |
Meltling Process Route: | BEF + AOD / EAF + LF + VD / + ESR/VAR |
Standard Export Packing Way: | wooden box, Pallet |
Production Lead Time: | Within 25 days after downpayment. |
Description
|
Turbine blade steel ASTM A565 Grade 616 ( Equivalent to SS422, 1.4935 S42200) is usually produced by AOD / EAF followed by electroslag refining ESR if necessary for Military or Civil use.
Major applications and features for this type of grade
Forms and Shapes availableChemical equipment & pats. Mechanical parts used in the condition of corrosion resistance. Automobile parts, exhaust pipe, Electronics, Turbine motor blade. Bolt and nut, Valve, Pressure vessel. Engine components. High strength and boat propeller shafts. Plastic moulding dies Corrosion resistant Heat resistant quality Polishing performance Heat Treatment Practice Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements. Chemical Composition (Mass weight %): C (%): 0.20 ~ 0.25, Si (%): ≤ 0.50, Mn (%): 0.50 ~ 1.00, P (%)≤: 0.025 S (%)≤: 0.015, Cr (%): 11.0 ~ 12.5, Ni (%): 0.50 ~ 1.00, Mo (%): 0.90 ~ 1.25 W (%): 0.90 ~ 1.25, V (%): 0.20 ~ 0.30 Mechanical Properties at room temp. Condition of heat treatment: Annealed Tensile strength, σb ≥/MPa: - Yield strength, σ0.2 ≥/MPa:- Elongation, < δ ≥(%): - Reduction of area, ф ≥(%): - Hardness | HRS: ≤ 248 Condition of heat treatment: + T, middle tempered Tensile strength, σb ≥/MPa: - Yield strength, σ0.2 ≥/MPa:- Elongation, δ ≥(%): - Reduction of area, ф ≥(%): - Hardness | HRS: ≤ 285 Condition of heat treatment: HT 1022℃ ~ 1050℃ air or oil cooled, ≥620℃ X 2H, tempered Tensile strength, σb ≥/MPa: 965 Yield strength, σ0.2 ≥/MPa: 760 Elongation, δ ≥(%): 13.0 Reduction of area, ф ≥(%): 30.0 Hardness | HRS: 302 ~ 352 Condition of heat treatment: H 1022℃ ~ 1050℃ air or oil cooled, ≥677℃ X 2H, tempered Tensile strength, σb ≥/MPa: 825 Yield strength, σ0.2 ≥/MPa: 585 Elongation, δ ≥(%): 17.0 Reduction of area, ф ≥(%): 35.0 Hardness | HRS: 241 ~ 285 Round bar (Diameter): 5.5 mm to 700 mm Wire rod (Diameter): 0.10 ~ 16mm Square bar / Flat bar: 5mm to 550mm Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form) Forged ring: OD200 ~ 1500mm X ID150 ~ 1250mm X H20 ~ 1250mm Heavy/middle plate via hot rolled: T50 - 200mm X W80- 1200mm X L1000-3000mm Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM. |